TOTAL PRO GF-10 1.75
€52.00
Tax included
TOTAL PRO GF-10 is impact-resistant glass-filled (10%) TPU-based composite with heat resistance up to 110°C for printing large gears, durable housings, mechanically loaded parts, aerodynamic body kits for cars.
It has high chemical resistance to acid and alkali solutions, fats, oils, xylene, diesel fuel. Limited to gasoline, kerosene, acetone, dichloromethane..
Due to low shrinkage (up to 0.9%), good interlayer adhesion and high abrasive resistance, TOTAL PRO GF-10 plastic will be an excellent alternative to polyamides-based composites..
Perfectly amenable to drilling, threading..
For best results, it is recommended to dry for 2-3 hours before printing at a temperature of 60-70°C. .
ATTENTION! Plastic is abrasive, it is recommended to print using a steel nozzle.
369918465081
1 Items
Data sheet
- Bed temperature
- 60-100°
- Density
- ~1.4 g/cm3
- blowing
- if necessary 20-60%
- Nozzle temperature
- 230-250°C
- Print speed
- до 100 mm/s
- Filament feed
- 95-100%
- Nozzle diameter
- up to 0.4 mm (min)
- Min. layer height
- 0.1 mm
- Temperature resistance (min/max)
- от -50 до +110°С
- Bar diameter tolerance
- 0.03 mm
- Quantity per reel
- 250 m
- Shore D hardness
- 85
- Elongation at break
- 15%
- Tensile modulus
- 3000 MPa
- Vicat softening temperature
- 110°C
- Maximum breaking strength
- ~75 MPa
- Shrinkage in the manufacture of products
- 0.5-0.9%
Comments (0)
No customer reviews for the moment.
TOTAL PRO GF-10 is impact-resistant glass-filled (10%) TPU-based composite with heat resistance up to 110°C for printing large gears, durable housings, mechanically loaded parts, aerodynamic body kits for cars.
It has high chemical resistance to acid and alkali solutions, fats, oils, xylene, diesel fuel. Limited to gasoline, kerosene, acetone, dichloromethane..
Due to low shrinkage (up to 0.9%), good interlayer adhesion and high abrasive resistance, TOTAL PRO GF-10 plastic will be an excellent alternative to polyamides-based composites..
Perfectly amenable to drilling, threading..
For best results, it is recommended to dry for 2-3 hours before printing at a temperature of 60-70°C. .
ATTENTION! Plastic is abrasive, it is recommended to print using a steel nozzle.